injection mold Ningbo beilun daqi dongfeng mold plastic Factory

injection mold,plastic injection mold--dongfeng mold

Home
About us
Where You Live
Arafat smart shade
Plastic Mold
Casting Mold
Stamping Mold
Auto Settings
Other mold
Workroom
Mold News
Mold FAQ
Contact us
Sales Network
Chinese Version

Guestbook
How to improve Web site needs, please message

E-mail:
Message:

    
Friendlink
[link]
casting mold 06 E-mail: dfmould@dfmould.com.cn
casting mold 06

The problem of mold powder entrapment in molten steel in a continuous casting mold continues to be a serious obstacle to the producing of clean steel. Four types of the mechanisms of mold powder entrapment have been proposed on the basis of water model experiments. These mechanisms, however, cannot fully explain the size distribution of mold powder in the finished steel products. In this study, another type of entrapment mechanism was proposed. Namely, when the molten steel flow crosses the immersion nozzle, the pressure on the forward stagnation point increases, while that on the rear stagnation point decreases. As a result, the mold powder moves downwards along the rear surface of the immersion nozzle. If the mold powder reaches one of the ports of the immersion nozzle, it is sucked into the discharging molten steel flow, which causes significant mold powder entrapment. In order to ascertain the validity of this proposed mechanism, water model experiments were carried out using various kinds of silicone oils and salt water. The results of the model experiments revealed the possibility that the mold powder entrapment based on the mechanism proposed in this study takes place in the real continuous casting mold.

injection molding | plastic injection mold | Plastic Mold | Casting Mold | Stamping Mold | Auto Settings | pressing mold

Sales Network | Sitemap | XML | Links | Ningbo beilun daqi dongfeng mold plastic Factory All rights reserved.
http://www.nbmold.net Technocil Support:Seo